Typical superparamagnetism with improved electrical properties of nano modified bismuth ferrite multiferroic composites

Multiferroic composites with the chemical formula, (0.5) BiFeO₃ + (0.5) Ni_0.5Zn_0.5Fe₂O₄, in bulk and nano forms were synthesized by preparing bismuth ferrite (BiFeO₃ or BFO) in bulk (B) and nano (N) forms and nickel zinc ferrite (Ni_0.5Zn_0.5Fe₂O₄or NZFO) in nano form. Single phase BFO was synthesized using conventional solid-state reaction as well as sol-gel autocombustion methods and NZFO powders were prepared by using sol-gel autocombustion method, respectively. X-ray diffraction (XRD) studies reveal the existence of rhombohedrally distorted perovskite structure for BFO and cubic spinel phase for NZFO in single phase as well as composite samples. Microstructural studies and energy dispersive spectroscopy (EDS) data reveal the formation of grains, intergranular porosities and chemical purity of the synthesized samples. Dielectric and AC conductivity measurements confirm the existence of space charge polarization along with the small polaron model in these composites. Ferroelectric and magnetic studies show that there was a considerable enhancement in the ferroelectric and magnetic orders for the nano form of the BFO (N) + NZFO composite. The observed remnant polarization values 2.80388 & 7.75901 μC/cm², saturation magnetization values 37.96072 & 40.47491emu/gm for bulk BFO (B) + NZFO and nano BFO (N) + NZFO composites, respectively. Interestingly, both the samples exhibit superparamagnetic behaviour at room temperature with coercivities close to zero. This typical behaviour is attributed to the corresponding anisotropic contributions originated from the individual constituents. The observed variations in BFO (N) + NZFO sample attributed to the corresponding structural modifications brought about by the variations due to its size effect in the present work.