MOR/SBA-15复合分子筛的合成、表征及其催化性能评价
引用本文:韩海波,王有和,李康,雷杰,刘丹禾,阎子峰.MOR/SBA-15复合分子筛的合成、表征及其催化性能评价[J].无机化学学报,2018,34(8):1477-1482.
作者姓名:韩海波  王有和  李康  雷杰  刘丹禾  阎子峰
作者单位:中国石油大学重质油国家重点实验室;中石化炼化工程集团洛阳技术研发中心
基金项目:国家自然科学基金(No.21776311)和中央高校基本科研业务费专项资金(No.15CX05030A)资助项目。
摘    要:采用MOR纳米晶和正硅酸四乙酯为硅源,P123三嵌段共聚物为模板剂水热合成MOR/SBA-15复合分子筛催化剂。采用XRD、SEM、TEM和EDX等手段对催化剂进行了表征,在固定床反应器中评价二甲醚制乙醇催化性能。结果表明,通过控制合适的MOR纳米晶种及MOR纳米晶种在SBA-15水热合成体系中的添加量,可以成功地将MOR纳米晶作为SBA-15的结构单元嫁接到SBA-15的介孔骨架中,水热合成的MOR/SBA-15复合分子筛催化剂同时具有MOR和SBA-15的XRD特征衍射峰,相比于SBA-15,其比表面积和总孔体积由756 m2·g~(-1),1.07 cm3·g~(-1)降低至628 m2·g~(-1),0.85 cm3·g~(-1),平均孔径由8.1 nm提高到9.3nm,Cu修饰的MOR/SBA-15复合分子筛催化剂同时具有Cu MOR羰基化和Cu SBA-15加氢的双功能催化性能,其催化剂评价结果显示二甲醚转化率为43.6%左右,乙醇选择性为95.3%,Cu MOR/SBA-15复合分子筛催化剂实现了二甲醚到乙醇的一步转化。

关 键 词:MOR纳米晶  MOR/SBA-15复合分子筛  二甲醚  双功能催化
收稿时间:2018/3/27 0:00:00
修稿时间:2018/5/7 0:00:00

Synthesis, Characterization and Catalytic Performance of MOR/SBA-15 Composite Zeolite
HAN Hai-Bo,WANG You-He,LI Kang,LEI Jie,LIU Dan-He and YAN Zi-Feng.Synthesis, Characterization and Catalytic Performance of MOR/SBA-15 Composite Zeolite[J].Chinese Journal of Inorganic Chemistry,2018,34(8):1477-1482.
Authors:HAN Hai-Bo  WANG You-He  LI Kang  LEI Jie  LIU Dan-He and YAN Zi-Feng
Institution:State Key Laboratory for Heavy Oil Processing, China University of Petroleum, Qingdao, Shandong 266580, China;Luoyang R & D Center of Technology of SINOPEC Engineering(Group) Co., Ltd., Luoyang, Henan 471003, China,State Key Laboratory for Heavy Oil Processing, China University of Petroleum, Qingdao, Shandong 266580, China,Luoyang R & D Center of Technology of SINOPEC Engineering(Group) Co., Ltd., Luoyang, Henan 471003, China,Luoyang R & D Center of Technology of SINOPEC Engineering(Group) Co., Ltd., Luoyang, Henan 471003, China,Luoyang R & D Center of Technology of SINOPEC Engineering(Group) Co., Ltd., Luoyang, Henan 471003, China and State Key Laboratory for Heavy Oil Processing, China University of Petroleum, Qingdao, Shandong 266580, China
Abstract:The hydrothermal synthesis of MOR/SBA-15 composite zeolite has been achieved by employing MOR nanocrystalline and tetraethyl orthosilicate (TEOS) as silica source, and triblock copolymer P123 as hard template. The catalyst was characterized through an integrated method including XRD, SEM, TEM and EDX, and the corresponding catalytic performance was evaluated in the conversion of diethyl ether (DME) to ethanol in a fixed-bed reactor. The results show that MOR nanocrystalline, a building unit for SBA-15, can be successfully grafted in the mesopore framework of SBA-15 by controlling the addition of MOR nanocrystalline. The obtained composite zeolite possesses both the characteristic diffraction peaks of MOR and SBA-15. The specific surface area and total pore volume, compared with SBA-15, decrease from 756 m2·g-1, 1.07 m3·g-1 to 628 m2·g-1, 0.85 m3·g-1, respectively. And the pore diameter in average raises from 8.1 to 9.3 nm. An extra Cu modification of the composite zeolite allows a bifunctional catalytic performance of carbonylation with CuMOR and hydrogenation with CuSBA-15. The catalyst evaluation tests show that the conversion of DME is 43.6% and the selectivity to ethanol is 95.3%, indicating a one-step transformation from DME to ethanol over CuMOR/SBA-15 composite zeolite.
Keywords:MOR nano crystalline  MOR/SBA-15 composite zeolite  MDE  bifunctional catalyst
本文献已被 CNKI 等数据库收录!
点击此处可从《无机化学学报》浏览原始摘要信息
点击此处可从《无机化学学报》下载免费的PDF全文
设为首页 | 免责声明 | 关于勤云 | 加入收藏

Copyright©北京勤云科技发展有限公司  京ICP备09084417号