Structural and optical properties of thin films prepared from surface modified ZrO2

This paper describes the preparation and characterization of ZrO₂ thin films deposited on silicon wafer by spin coating method. Nanocrystalline ZrO₂ was synthesized by hydrothermal method using zirconium (IV)-n-propoxide as a precursor material. Surface of the ZrO₂ particles was then modified with 2-acetoacetoxyethyl methacrylate used as a copolymer for coatings. The optical properties, nanostructure and surface morphology of the thin films prepared from surface modified ZrO₂ nanoparticles were examined by optical spectroscopy, X-ray diffraction and scanning electron microscopy, respectively. It was found that the films deposited on silicon wafer have crystalline structure of monoclinic (111) at temperature of 150 °C. It was observed that films depict very dense material that does not present any granular or columnar structure. It was found that optical transparency of thin ZrO₂ films distributed in the range of 30-40 percent in the spectral range 400-800 nm. Refractive index of ZrO₂ films were determined as functions of ZrO₂ content and it was found that the refractive index increases from 1.547 to 1.643 with increased ZrO₂ content.