INFLUENCE OF LOADING RATE ON DYNAMIC FRACTURE BEHAVIOR OF FIBER-REINFORCED COMPOSITES |
| |
作者单位: | LTCS and College of Engineering,Peking University,Beijing 100871,China |
| |
基金项目: | 国家自然科学基金
|
| |
摘 要: | The effect of loading rate on the dynamic fracture properties and the failure mechanisms of glass fiber-reinforced composite materials under mode I fracture is studied. Dynamic reflective caustic experiments are carried out for two loading rates. By measuring the characteristic dimensions of the shadow spots during the caustic experiments, the dynamic SIFs are calculated for different loading rates. The experimental results indicate that the dynamic fracture toughness Kid increases remarkably with increasing loading rate, and the crack grows faster under the high-velocity impact. Moreover, by examining the crack growth routes and the fracture surfaces, it is shown that the loading rate also greatly affects the failure mechanisms at micro-scale.
|
关 键 词: | 焦散线法 纤维加固材料 断裂 负载率 |
收稿时间: | 11 April 2008 |
INFLUENCE OF LOADING RATE ON DYNAMIC FRACTURE BEHAVIOR OF FIBER-REINFORCED COMPOSITES |
| |
Authors: | Kezhuang Gong Zheng Li Weizhong Qin |
| |
Institution: | LTCS and College of Engineering, Peking University, Beijing 100871, China |
| |
Abstract: | The effect of loading rate on the dynamic fracture properties and the failure mechanisms of glass fiber-reinforced composite materials under mode I fracture is studied. Dynamic reflective caustic experiments are carried out for two loading rates. By measuring the characteristic dimensions of the shadow spots during the caustic experiments, the dynamic SIFs are calculated for different loading rates. The experimental results indicate that the dynamic fracture toughness KId increases remarkably with increasing loading rate, and the crack grows faster under the high-velocity impact. Moreover, by examining the crack growth routes and the fracture surfaces, it is shown that the loading rate also greatly affects the failure mechanisms at micro-scale. |
| |
Keywords: | caustics method fiber-reinforced material mode I fracture loading rate |