接触应力对轮轨材料滚动摩擦磨损性能影响
引用本文:王文健,郭俊,刘启跃.接触应力对轮轨材料滚动摩擦磨损性能影响[J].摩擦学学报,2011,31(4):352-356.
作者姓名:王文健  郭俊  刘启跃
作者单位:西南交通大学牵引动力国家重点实验室摩擦学研究所,四川成都,610031
基金项目:国家科技支撑计划项目(2009BAG12A01-B05-1)和国家重点基础研究发展计划项目(973)(2007CB714702)
摘    要:利用MMS-2A型微机控制摩擦磨损试验机研究了接触应力对轮轨材料的滚动摩擦磨损性能影响.结果表明:随接触应力的增加,滚动摩擦系数呈增加趋势,车轮和钢轨试样磨损加剧;相同接触应力水平下,车轮试样磨损量大于钢轨试样,表面损伤严重;随接触应力的增加,车轮试样表面从犁沟且轻微剥落向严重剥落损伤转变,钢轨试样表面损伤主要表现为犁沟效应并伴随有剥落现象,但相比车轮试样的剥离损伤要轻微.

关 键 词:滚动磨损  车轮  钢轨  磨损机制  接触应力

Effect of Contact Stress on Rolling Friction and Wear Behavior of Wheel-rail Materials
WANG Wen-jian,GUO Jun and LIU Qi-yue.Effect of Contact Stress on Rolling Friction and Wear Behavior of Wheel-rail Materials[J].Tribology,2011,31(4):352-356.
Authors:WANG Wen-jian  GUO Jun and LIU Qi-yue
Institution:Tribology Research Institute, State Key Laboratory of Traction Power, Southwest Jiaotong University, Chengdu 610031, China;Tribology Research Institute, State Key Laboratory of Traction Power, Southwest Jiaotong University, Chengdu 610031, China;Tribology Research Institute, State Key Laboratory of Traction Power, Southwest Jiaotong University, Chengdu 610031, China
Abstract:The effect of contact stress on rolling friction and wear behavior of wheel/rail materials were investigated using a MMS-2A testing apparatus. The results show that the rolling friction coefficient would increase with the increase of contact stress, which resulted in the aggravation of wheel/rail wear. The wear volume of wheel specimen was larger than that of rail specimen under the same contact stress condition. Furthermore, the surface damage of wheel specimen was more severe. With the increase of contact stress, the damage of wheel specimen changed from the plough with slight delamination to serious spalling damage. However, the plough with spalling phenomena was dominant for the damage of rail specimen. But the spalling damage of rail specimen was more slight than that of wheel specimen.
Keywords:rolling wear  wheel  rail  wear mechanism  contact stress