Effect of Ag addition on the third-order nonlinearity and physicochemical property of chalcohalide glass

In this work, the 70GeS₂–20In₂S₃–10CsI glass introduced with 0–10 mol% Ag₂S were prepared by the vacuumed melt-quenching technique. The physicochemical properties, such as glass transition temperature, density, refractive index, transmittance, hardness as well as third-order nonlinearity are investigated with the increasing Ag₂S contents. It was found that the refractive index (@632.8 nm), density, and hardness of glasses increase distinctly from 2.204 to 2.270, from 3.520 to 3.675 g cm⁻³ and from 180.9 to 227.9 kg mm⁻², respectively. Meanwhile, the nonlinear refractive index increases from 3.2 × 10⁻¹⁸ to 4.6 × 10⁻¹⁸ m²/W due to the increased refractive index. Finally, the Raman spectra are performed to structurally illustrate the role of Ag addition on the changes of the physicochemical properties. With the Ag₂S contents increasing, the vibration intensity of the InS₄] and InS₃I] tetrahedrons increases and the heavy Ag atoms result in the increased density and refractive index, as well as the nonlinear refractive index. The Ag-containing glass, which exhibited good thermal stability, excellent infrared transparency and ultrafast nonlinear optical properties, can be find applications for the IR window material or ultrafast infrared optics.