Enhanced dielectric and nonohmic properties of SrTiO3-modified CaCu3Ti4O12 ceramics

Dielectric and nonohmic properties of CaCu₃Ti₄O₁₂ (CCTO) ceramics can be modified by addition of SrTiO₃ (STO) in different molar proportions which were fabricated by a modified sol-gel method. XRD results indicated that all modified ceramics showed mixed phase consisting of both CCTO and STO. SEM images and grain size distribution probability also presented the change of microstructure with the addition of STO. The dielectric loss of the CCTO/0.4STO ceramics sintered at 1000 °C can be lower than 0.02 in a wide frequency (1 kHz–10 kHz), especially at 1 kHz, the dielectric loss of this sample is as low as 0.012. Furthermore, excellent nonlinear I–V electrical characteristic (high breakdown voltage to 54.15 kV/cm for CCTO/0.4STO sintered at 1000 °C) was observed as well. All the results indicated that the addition of STO does improve the dielectric properties and nonohmic characteristics of CCTO ceramics dramatically.