Dielectric and piezoelectric properties of PZT–cement composites

Lead zirconate titanate (PZT) and cement composites of 0–3 connectivity were produced using PZT of 30–90% by volume. The effects of PZT on dielectric and piezoelectric properties of the composites were then investigated. The dielectric constant (ε_r) of the composites was found to increase with increasing PZT content. The ε_r value of 90% PZT composite obtained was 291 which is noticeably higher than that of PC sample (ε_r = 79). The dielectric loss (tan δ) was found to decrease with PZT content and the tan δ value was lowest at 0.63 for 90% PZT composite. Piezoelectric coefficient (d₃₃) was found to increase with PZT content as expected. However, the effects were most significant at two stages, first at 30% PZT volume content (14 pC/N) and then at very high PZT content (90% by volume) where d₃₃ value reached 43 pC/N.