Electrochemical characterization of ionic liquid based gel polymer electrolyte for lithium battery application

High molecular weight polymer poly(vinylidenefluoride-co-hexafluoropropylene) (PVdF-HFP), ionic liquid 1-ethyl-3-methylimidazolium bis(fluorosulfonyl)imide (EMIMFSI), and salt lithium bis(trifluoromethanesulfonyl)imide (LiTFSI)-based free-standing and conducting ionic liquid-based gel polymer electrolytes (ILGPE) have been prepared by solution cast method. Thermal, electrical, and electrochemical properties of 80 wt% IL containing gel polymer electrolyte (GPE) are investigated by thermogravimetric (TGA), impedance spectroscopy, linear sweep voltammetry (LSV), and cyclic voltammetry (CV). The 80 wt% IL containing GPE shows good thermal stability (~?200 °C), ionic conductivity (6.42?×?10^?4 S cm^?1), lithium ion conductivity (1.40?×?10^?4 S cm^?1 at 30 °C), and wide electrochemical stability window (~?4.10 V versus Li/Li⁺ at 30 °C). Furthermore, the surface of LiFePO₄ cathode material was modified by graphene oxide, with smooth and uniform coating layer, as confirmed by scanning electron microscopy (SEM), and with element content, as confirmed by energy dispersive X-ray (EDX) spectrum. The graphene oxide-coated LiFePO₄ cathode shows improved electrochemical performance with a good charge-discharge capacity and cyclic stability up to 50 cycles at 1C rate, as compared with the without coated LiFePO₄. At 30 °C, the discharge capacity reaches a maximum value of 104.50 and 95.0 mAh g^?1 for graphene oxide-coated LiFePO₄ and without coated LiFePO₄ at 1C rate respectively. These results indicated improved electrochemical performance of pristine LiFePO₄ cathode after coating with graphene oxide.