| Large third—order optical nonlinearity in Au nanomeytre particle doped BaTiO3 composite films near the resonant frequency |
| |
| 引用本文： | 王伟田,杨光,陈正豪,周岳亮,吕惠宾,杨国桢.Large third—order optical nonlinearity in Au nanomeytre particle doped BaTiO3 composite films near the resonant frequency[J].中国物理 B,2002,11(12):1324-1327. |
| |
| 作者姓名： | 王伟田 杨光 陈正豪 周岳亮 吕惠宾 杨国桢 |
| |
| 作者单位： | Laboratory of Optical Physics, Institute of Physics and Centre for Condensed Matter Physics, Chinese Academy of Sciences, Beijing 100080, China;Laboratory of Optical Physics, Institute of Physics and Centre for Condensed Matter Physics, Chinese Academy of Sciences, Beijing 100080, China;Laboratory of Optical Physics, Institute of Physics and Centre for Condensed Matter Physics, Chinese Academy of Sciences, Beijing 100080, China;Laboratory of Optical Physics, Institute of Physics and Centre for Condensed Matter Physics, Chinese Academy of Sciences, Beijing 100080, China;Laboratory of Optical Physics, Institute of Physics and Centre for Condensed Matter Physics, Chinese Academy of Sciences, Beijing 100080, China;Laboratory of Optical Physics, Institute of Physics and Centre for Condensed Matter Physics, Chinese Academy of Sciences, Beijing 100080, China |
| |
| 基金项目： | Project supported by the National Natural Science Foundation of China (Grant No 5001161952). |
| |
| 摘 要： | Nanometre-sized gold particles embedded in BaTiO3 composite thin films (Au/BaTiO3) were fabricated by the pulsed laser deposition technique. The films were grown on MgO (100) substrates at 700℃. The crystalline property of the films was studied with x-ray diffraction. X-ray photoelectron spectroscopy was used to check the Au composition and chemical nature for the deposited films. The absorption peak due to the surface plasmon resonance of Au particles was observed at the wavelength of about 570 nm, which increased as the metal particle size was increased. The nonlinear optical properties of the Au/BaTiO3 films were determined using the z-scan method at the wavelength of 532 nm, which was close to the resonant frequency. The real and imaginary parts of the third-order nonlinear susceptibility χ(3) at an Au concentration of about 6.7 at.% were determined to be 6.62×10-7 esu and -6.24×10-8 esu, respectively. The films showed a very large absorption, masking the nonlinear refraction effect at high metal concentrations.
|
| 关 键 词： | 钛酸钡薄膜 金纳米粒子 非线性光学 |
| 收稿时间： | 7/3/2002 12:00:00 AM |
Large third-order optical nonlinearity in Au nanometre particle doped BaTiO3 composite films near the resonant frequency |
| |
| Abstract: | |
| |
| Keywords: | Au/BaTiO3 susceptibility z-scan pulsed laser deposition |
|
| 点击此处可从《中国物理 B》浏览原始摘要信息 |
| 点击此处可从《中国物理 B》下载免费的PDF全文 |
|