Effect of Bi-substitution on the dielectric properties of polycrystalline yttrium iron garnet
Authors:Hongjie Zhao  Ji Zhou  Yang Bai  Zhilun Gui  Longtu Li
Institution:

Department of Materials Science and Engineering, State Key Laboratory of New Ceramics and Fine Processing, Tsinghua University, Beijing 100084, People's Republic of China

Abstract:The effect of Bi-substitution on the dielectric properties of yttrium iron garnet (YIG) was studied in this paper. The Bi-substituted YIG (YIG:Bi) polycrystalline samples, having composition of Y3?xBixFe5O12, were prepared by the solid-state reaction method. x varied from 0 to 1.2. The phase formation and microstructure were performed by X-ray diffraction and scanning electron microscopy, respectively. Ions valency was identified by X-ray photoelectron spectroscopy. The impedance analyzers are used to measure the frequency dependence and the temperature dependence of relative dielectric constant (var epsilonr) and loss tangent (tan δ). The experimental results show that the Bi-substitution lowers the phase formation and sintering temperature. Electronic carrier concentration drops dramatically due to limitation of ferric valency variation. Hence, var epsilonr and tan δ decrease with addition of Bi. Dispersion characteristic indicates non-Debye-type dispersion. A maximum of var epsilonr appears as the temperature rises.
Keywords:Yttrium iron garnet  Bi-substitution  Dielectric properties  Low temperature sintering
本文献已被 ScienceDirect 等数据库收录!
设为首页 | 免责声明 | 关于勤云 | 加入收藏

Copyright©北京勤云科技发展有限公司  京ICP备09084417号