用显微红外光谱法研究高分子共混物溶液自组织形成的相组成分布

本文制备了ＰＳ／ＰＣ（７／３）和ＰＳ／ＰＭＭＡ（５／５）的四氢呋喃（ＴＨＦ）溶液，通过缓慢蒸发溶剂制得ＰＳ／ＰＣ和ＰＳ／ＰＭＭＡ的共混物薄膜。利用不同的ＦＴＩＲ测试方法检测了制得薄膜中的组成分布。将ＰＳ／ＰＣ薄膜超薄切片，通过显微投射红外方法检测了其纵剖面的组成分布（测试步长为１６μｍ）。结果表明：ＰＳ含量从膜底面到表面缓慢增大呈梯度分布，在膜表面附近急剧增大，即ＰＳ组分在成膜过程中向表面（与空气

Determination of the Composition Distribution of Polymer Blend Films by Using Microscopic FTIR

In this paper, PS/PC blend film (about 120 microns thick) and PS/PMMA (about 90 microns thick) blend film were prepared by evaporation the solvent very slowly from polymer blend solution. Different FTIR methods were used to determine the composition distribution along the vertical direction of the films. PS/PC film was firstly sectioned by ultramicrotomy, then the vertical section was measured to determine the composition of every 16 microns width unit from the surface-side to the bottom-side by Microscopic transmission-FTIR. The results showed that the concentration of PS was significantly greater in the vicinity of the surface of the film than that in the bulk, i.e., the component of PS enriched to the surface. Focusing the reflecting infrared light on different layer of the film, we can detect the composition of the different depth region in the PS/PMMA blend film. As the result, PMMA aggregated to the bottom of the film. It was considered that this effect was related to the different affinity and wetting prosperities of the blend component to the substrate or air.