| 基于在聚合物中掺杂染料DCJTB的白色有机电致发光器件 |
| |
| 引用本文： | 张妍斐,徐征,张福俊,王勇,赵谡玲.基于在聚合物中掺杂染料DCJTB的白色有机电致发光器件[J].光谱学与光谱分析,2008,28(4):760-762. |
| |
| 作者姓名： | 张妍斐 徐征 张福俊 王勇 赵谡玲 |
| |
| 作者单位： | 北京交通大学光电子技术研究所，北京交通大学发光与光信息技术教育部重点实验室，北京 100044 |
| |
| 基金项目： | 国家自然科学基金
,
国家高技术研究发展计划(863计划)
,
国家重点基础研究发展计划(973计划)
,
国家自然科学基金
,
北京市科技新星计划项目
,
北京交通大学校科研和教改项目 |
| |
| 摘 要： | 将Alq3和DCJTB作为掺杂物与基质PVK按照不同比例混合共溶，旋涂成膜，制备了PVK∶Alq3∶DCJTB为发光层的结构为ITO/ PVK∶Alq3∶DCJTB/ BCP/Alq3/LiF/Al的器件，其中Alq3和BCP分别用作电子传输层和空穴阻挡层，PVK用作蓝光发光层和空穴传输层。保持PVK和DCJTB的质量比为100∶1不变，改变PVK和 Alq3的质量比，当PVK和Alq3的质量比为20∶1时，得到了效果较好的白光。器件在电压为14 V时，色坐标达到(0.33，0.36)，在10～14 V范围内变化甚微。
|
| 关 键 词： | 白光 能量传递 有机材料 |
| 文章编号： | 1000-0593(2008)04-0760-03 |
| 收稿时间： | 2006-11-08 |
| 修稿时间： | 2006年11月8日 |
White Organic Light Emitting Device with Dyestuff DCJTB Blended in Polymer |
| |
| ZHANG Yan-fei,XU Zheng,ZHANG Fu-jun,WANG Yong,ZHAO Su-ling.White Organic Light Emitting Device with Dyestuff DCJTB Blended in Polymer[J].Spectroscopy and Spectral Analysis,2008,28(4):760-762. |
| |
| Authors: | ZHANG Yan-fei XU Zheng ZHANG Fu-jun WANG Yong ZHAO Su-ling |
| |
| Institution: | Institute of Optoelectronic Technology, Beijing Jiaotong University, Key Laboratory of Luminescence and Optical Information, Beijing Jiaotong University, Ministry of Education，Beijing 100044, China |
| |
| Abstract: | The Alq3 and DCJTB were blended with poly (N-vinylcarbazole) (PVK) in different weight ratios and spin coated into films. Multilayer devices with the light emitting layer PVK : Alq3 : DCJTB were fabricated, and their structure was ITO/ PVK : Alq3 : DCJTB/ BCP/Alq3/LiF/Al in which BCP and Alq3 were employed as the hole-blocking and electron-transporting layers respectively, PVK is the blue light-emitting as well as hole-transporting layer. The mass proportion of PVK relative to Alq3 was tuned while the quality ratio of PVK to DCJTB remained (100 : 1). Finally, fairly pure and stabile white emission was achieved when PVK : Alq3 : DCJTB was 100 : 5 : 1. The CIE coordinate was (0.33, 0.36) at 14 V, which is very stable at various biases (10-14 V). |
| |
| Keywords: | White light Energy transfer Organic materials |