氯化镧与聚氨酯相互作用的FTIR研究
引用本文:刘智,刘新海,曹赤诚,孙贤育,翁诗甫,徐端夫,吴瑾光.氯化镧与聚氨酯相互作用的FTIR研究[J].光谱学与光谱分析,2004,24(5):536-538.
作者姓名:刘智  刘新海  曹赤诚  孙贤育  翁诗甫  徐端夫  吴瑾光
作者单位:1. 北京大学化学与分子工程学院,稀土材料化学及应用国家重点实验室,北京,100871
2. 中国科学院化学研究所高分子物理与化学国家重点实验室,北京,100080
3. 北京联合大学应用文理学院,北京,100038
基金项目:国家重点基础研究发展规划(G1998061307, 2002CCA01900), 国家自然科学基金(39730160, 50103001)资助项目
摘    要:将LaCl3 掺入PU制得LaCl3 /PU复合体系。DSC的结果显示LaCl3 的加入使得PU体系的相转变行为发生了变化 ,位于 11 5 8℃的吸热峰消失。通过FTIR研究表明 :La3 与PU体系内的羰基发生了络合配位作用 ,使得PU的氢键结构体系发生了变化 ,峰位分别由 16 33和 3311cm-1蓝移至 16 4 7和 335 5cm-1。远红外光谱的中 2 0 0cm-1峰的出现也进一步证明了La—O键的形成。这为PU与氯化镧的络合作用的存在提供了直接的证据。

关 键 词:改性聚氨酯  稀土  红外光谱(FTIR)  示差扫描量热仪(DSC)
文章编号:1000-0593(2004)05-0536-03
修稿时间:2003年8月16日

The Interaction between La and Polyurethane System
Zhi Liu,Xin-hai Liu,Chi-cheng Cao,Xian-yu Sun,Shi-fu Weng,Duan-fu Xu,Jin-guang Wu.The Interaction between La and Polyurethane System[J].Spectroscopy and Spectral Analysis,2004,24(5):536-538.
Authors:Zhi Liu  Xin-hai Liu  Chi-cheng Cao  Xian-yu Sun  Shi-fu Weng  Duan-fu Xu  Jin-guang Wu
Institution:The State Key Laboratory of Rare Earth Materials Chemistry and Applications, College of Chemistry and Molecular Engineering, Peking University, Beijing 100871, China.
Abstract:A series of polyether polyurethane (PU)-LaCl3 composites with different lanthanum contents were prepared. DSC results indicate that LaCl3 promotes phase transition behavior of the LaCl3/PU composites, which causes the endothermic peak at 11.58 degrees C to disappear. FTIR spectroscopy demonstrates that significant variation can be observed. The peak at 1633 cm(-1) attributed to carbonyl vibration and the peak at 3311 cm(-1) attributed to N-H stretching band moves to 1647 cm(-1) and 3355 cm(-1), respectively, when LaCl3 is introduced into the PU system. A new band (-200 cm(-1)) assigned to the La-O band was observed, and the far IR result provided a direct evidence of the coordination between La3+ ion and C=O group of PU system.
Keywords:Modified polyurethane  Lanthanide  FTIR  DSC