溶胶凝胶燃烧合成法制备Y_2O_3∶RE(RE=Er或Er/Yb)上转换发光材料

采用溶胶凝胶燃烧合成法制备了稀土掺杂Y2O3粉体,考察了煅烧温度、Er3+浓度和Yb3+浓度对粉体发光性能的影响。研究结果表明,在800℃的温度下可以得到结晶良好的单相Y2O3粉体;随着煅烧温度的升高,样品结晶度越高,其上转换发光强度变强;在900℃的煅烧温度下,样品的粒径大约为lμm左右,颗粒尺寸分布较均匀;当Er3+掺杂浓度达到1mol%时,绿光发射强度达到最大值,而对于红光发射,其发射强度的最大值出现在4mol%的掺杂浓度;当Yb3+与Er3+掺杂比例达到4:1时,绿光发射强度达到最大值,而红光发射强度随着Yb3+浓度的增加一直增强。

Up-conversion luminescent materials of Y2O3: RE(RE=Er or Er/Yb) prepared by sol-gel combustion synthesis

Y2O3 powders doped with rare-earth ions were synthesized by sol-gel combustion synthesis. Effects of different calcinating temperatures, Er+ doping concentration and Yb3+ doping concentration were investigated. It was shown that the single well crystallized Y2O3 powders could be obtained at 800 degrees C; as the calcinating temperature increased, the crystallinity and upconversion luminescence intensity were higher; the particle size was uniform around 1 microm at 900 degrees C; when Er3+ doping concentration was 1 mol%, the green upconversion luminescence intensity reached the maximum, but for red upconversion luminescence, when Er3+ doping concentration was 4 mol%, its luminescence intensity reached the maximum; as the ratio of Yb3+ to Er3+ was 4:1, the green emission intensity reached the maximum, while the red emission intensity was always increasing as Yb3+ doping concentration increased.