颜面赝复体粘接剂的红外光谱分析

传统的颜面赝复体粘接剂按其成分可分为聚丙烯酸酯类和有机硅类。以往对于颜面赝复体粘接剂性能的研究，多为粘接强度的测试，而有关这些粘接剂在粘接过程中的变化研究则较少见。文章测试了两种颜面赝复体粘接剂 (Epithane3及Secure2 Adhesive)在液态、半固态时的红外光谱。结果提示，Epithane3结固过程中有水分和残留氨的挥发，Secure2 Adhesive结固过程中表现为乙酸乙酯挥发。有机硅官能团是有机硅类和硅橡胶的粘接强度比聚丙烯酸酯类高的关键。两种粘接剂红外光谱主要吸收峰的峰位、峰形与结固前相同, 表明结固前后其主要化学成分和基本结构未发生变化。

FTIR Spectroscopic Studies of Facial Prosthetic Adhesives

According to the composition of the traditional facial prosthetic adhesives, most of adhesives can be classified into two categories: acrylic polymer-based adhesive and silicone-based adhesive. In previous studies, measurements of various mechanical bond strengths were carried out, whereas the functional groups of the adhesives were evaluated seldom during the adhesion. In the present study the analysis of two facial prosthetic adhesives (Epithane3 and Secure2 Adhesive) was carried out by using infrared spectroscopy. Two adhesives in the form of fluid or semisolid were submitted to FTIR spectroscopy, respectively. The results showed that water and ammonia residue volatilized during the solidification of Epithane3,and absorption peak reduction of carbonyl was due to the volatilization of acetate vinyl from Secure2 Adhesive. Similar silicone functional groups both in the silicone-based adhesive and in silicone elastomer could be the key to higher bond strength between silicone elastomer and skin with silicone-based adhesive. The position, shape of main absorption peaks of three adhesives didn’t change, which showing that their main chemicals and basic structures didn’t change during solidification.