Electrical and electrochemical properties of glass-ceramic electrolytes in the systems Li2S-P2S5-P2S3 and Li2S-P2S5-P2O5

Electrical and electrochemical properties of the 70Li₂S·(30 − x)P₂S₅·xP₂S₃ and the 70Li₂S·(30 − x)P₂S₅·xP₂O₅ (mol%) glass-ceramics prepared by the mechanical milling technique were investigated. Glass-ceramics with 1 mol% P₂S₃ and 3 mol% P₂O₅ showed the highest conductivity of 5.4 × 10^− 3 S cm^− 1 and 4.6 × 10^− 3 S cm^− 1, respectively. Moreover, these glass-ceramics showed higher electrochemical stability than the 70Li₂S·30P₂S₅ (mol%) glass-ceramic. From the XRD patterns of the obtained glass-ceramics, trivalent phosphorus and oxygen were incorporated into the Li₇P₃S₁₁ crystal. We therefore presume that the Li₇P₃S₁₁ analogous crystals, which were formed by incorporating trivalent phosphorus and oxygen into the Li₇P₃S₁₁ crystal, improve the electrical and electrochemical properties of the glass-ceramics. An all-solid-state cell using the 70Li₂S·29P₂S₅·1P₂S₃ (mol%) glass-ceramic as solid electrolyte operated under the high current density of 12.7 mA cm^− 2 at the high temperature of 100 °C. The cell showed an excellent cyclability of over 700 cycles without capacity loss.