| 紫外光固化阳离子复合胶粘剂的制备与表征 |
| |
| 引用本文： | 沈雁,杨文彬,李银涛,谢长琼,李迎军,程亚非,周元林,卢忠远.紫外光固化阳离子复合胶粘剂的制备与表征[J].强激光与粒子束,2011,23(4). |
| |
| 作者姓名： | 沈雁 杨文彬 李银涛 谢长琼 李迎军 程亚非 周元林 卢忠远 |
| |
| 作者单位： | 1. 西南科技大学 四川省非金属复合与功能材料省部共建国家重点实验室培育基地， 四川 绵阳 621010；2. 西南科技大学 材料科学与工程学院， 四川 绵阳 621010 |
| |
| 基金项目： | 国家自然科学基金，四川省非金属复合与功能材料省部共建国家重点实验室培育基地开放基金，西南科技大学核废物与环境安全国防重点学科实验室开放基金 |
| |
| 摘 要： | 以三芳基六氟磷酸硫鎓盐为引发剂，钛酸四异丙酯(TIP)为无机前驱体，3,4-环氧环己基甲基3,4-环氧环己基甲酸酯为单体，制备了含TiO2纳米结构的紫外光固化阳离子复合胶粘剂。通过原子力显微镜对复合胶粘剂形貌进行表征，研究了TIP含量对胶粘剂折射率和光透过率的影响。结果表明：TiO2无机相均匀地分散在胶粘剂的聚合物基体中，平均粒径约为20 nm；随着体系中TIP质量分数的变化，复合胶粘剂折射率为1.510 3~1.540 9可调；胶粘剂的光透过率随TIP质量分数增加略有减低，但当TIP含量高达40%时，光透过率维持在90%左右。
|
| 关 键 词： | 紫外光固化 阳离子聚合 复合胶粘剂 折射率 光透过率 |
| 收稿时间： | 1900-01-01; |
Preparation and characterization of UV-curable cationic composite adhesive |
| |
| Shen Yan,Yang Wenbin,Li Yintao,Xie Changqiong,Li Yingjun,Cheng Yafei,Zhou Yuanlin,Lu Zhongyuan.Preparation and characterization of UV-curable cationic composite adhesive[J].High Power Laser and Particle Beams,2011,23(4). |
| |
| Authors: | Shen Yan Yang Wenbin Li Yintao Xie Changqiong Li Yingjun Cheng Yafei Zhou Yuanlin Lu Zhongyuan |
| |
| Institution: | 1. State Key Laboratory Cultivation Base for Nonmetal Composite and Functional Materials,Southwest University of Science and Technology, Mianyang 621010, China;2. School of Materials Science and Engineering, Southwest University of Science and Technology, Mianyang 621010, China |
| |
| Abstract: | UV-curable cationic composite adhesives containing TiO2 nanostructures were prepared by using 3,4-epoxycyclohexylmethyl 3, 4-epoxycyclohexanecarboxylate(CE) as monomer, triphenylsulfonium hexafluorophosphate salt (PI-432) as photoinitiator and titanium isopropoxide (TIP) as inorganic precursor. The morphology of the composite adhesives was characterized by atom force microscopy (AFM). The effect of TIP content on refractive index and transmittance of adhesives were studied. The results show that TiO2 nanostructures, the average diameter of which is 20 nm or so, can be uniformly dispersed in polymers of composite adhesives. The refractive index of adhesives can be adjusted from 1.501 9 to 1.544 9 with the change of TIP content. The transmittance of adhesives has a slight reduce with the in |
| |
| Keywords: | cationic polymerization composite adhesive refractive index transmittance |