| Optical and magnetic properties of nitrogen ion implanted MgO single crystal |
| |
| 作者姓名： | 刘春明 顾海权 向霞 张焱 蒋勇 陈猛 祖小涛 |
| |
| 作者单位： | Department of Applied Physics,University of Electronic Science and Technology of China School of Physics,Peking University |
| |
| 基金项目： | Project supported by the National Natural Science Foundation of China (Grant No. 10904008) and the Foundation for Young Scholars of University of Electronic Science and Technology of China (Grant Nos. L08010401JX0806). |
| |
| 摘 要： | The microstructure,optical property and magnetism of nitrogen ion implanted single MgO crystals are studied. A parallel investigation is also performed in an iron ion implanted single MgO sample as a reference. Large structural,optical and magnetic differences are obtained between the nitrogen and iron implanted samples. Room temperature ferromagnetism with a fairly large coercivity field of 300 Oe (1Oe=79.5775 A/m),a remanence of 38% and a slightly changed optical absorption is obtained in the sample implanted using nitrogen with a dose of 1×1018 ions/cm2 . Tran- sition metal contamination and defects induced magnetism can be excluded when compared with those of the iron ion implanted sample,and the nitrogen doping is considered to be the main origin of ferromagnetism.
|
| 关 键 词： | nitrogen implanted MgO magnetism optical property microstructure |
| 收稿时间： | 2010-09-25 |
Optical and magnetic properties of nitrogen ion implanted MgO single crystal |
| |
| Liu Chun-Ming,Gu Hai-Quan,Xiang Xi,Zhang Yan,Jiang Yong,Chen Meng and Zu Xiao-Tao.Optical and magnetic properties of nitrogen ion implanted MgO single crystal[J].Chinese Physics B,2011,20(4):47505-047505. |
| |
| Authors: | Liu Chun-Ming Gu Hai-Quan Xiang Xi Zhang Yan Jiang Yong Chen Meng and Zu Xiao-Tao |
| |
| Institution: | Department of Applied Physics, University of Electronic Science and Technology of China, Chengdu 610054, China;Department of Applied Physics, University of Electronic Science and Technology of China, Chengdu 610054, China;Department of Applied Physics, University of Electronic Science and Technology of China, Chengdu 610054, China;School of Physics, Peking University, Beijing 100871, China;Department of Applied Physics, University of Electronic Science and Technology of China, Chengdu 610054, China;Department of Applied Physics, University of Electronic Science and Technology of China, Chengdu 610054, China;Department of Applied Physics, University of Electronic Science and Technology of China, Chengdu 610054, China |
| |
| Abstract: | The microstructure, optical property and magnetism of nitrogen ion implanted single MgO crystals are studied. A parallel investigation is also performed in an iron ion implanted single MgO sample as a reference. Large structural, optical and magnetic differences are obtained between the nitrogen and iron implanted samples. Room temperature ferromagnetism with a fairly large coercivity field of 300 Oe (1 Oe=79.5775 A/m), a remanence of 38% and a slightly changed optical absorption is obtained in the sample implanted using nitrogen with a dose of 1×1018 ions/cm2. Transition metal contamination and defects induced magnetism can be excluded when compared with those of the iron ion implanted sample, and the nitrogen doping is considered to be the main origin of ferromagnetism. |
| |
| Keywords: | nitrogen implanted MgO magnetism optical property microstructure |