Oriented Crystallization of Polyethylene in Compatible Blends with Polyamide 11

The oriented crystallization of polyethylene (PE) in uniaxially oriented films of compatible blends with polyamide 11 (PA11) was studied. The PE sample used was a random copolymer of PE with methacrylic acid (MAA), poly(ethylene-co-methacrylic acid) (PEMAA), with 4wt% MAA units. Oriented films of PA11/PEMAA blends were prepared by uniaxial drawing of the melt-mixed blends. The drawn films with fixed lengths were heat-treated at 120°C for 3min to melt the PE component, followed by cooling the sample to room temperature at a rate of 2°C/min to recrystallize the PE (designated slowly crystallized sample). The PE component crystallized in elongated domains of PEMAA with diameters of 0.5–2 μ m and lengths of 5–10 μ m for the PA11/PEMAA = 80/20 blend, resulting in the oriented crystallization of PE crystals. The crystal b-axis of PE was highly oriented in the direction perpendicular to drawing, while the crystal a-axis was weakly oriented in the drawing direction in the slowly crystallized sample of the PA11/PEMAA = 80/20 blend. The a-axis orientation of PE crystals in the PA11/PEMAA = 80/20 blend contributes to the improvement of mechanical properties in the direction perpendicular to drawing.