Miscibility,Morphology, and Thermal Properties of Poly(Trimethylene Terephthalate)/Polycarbonate

Abstract

Poly(trimethylene terephthalate)/polycarbonate (PTT/PC) blends were prepared by melt blending and rapid quenching in ice water. The miscibility and thermal properties were investigated using differential scanning calorimeter (DSC) and dynamic mechanical analysis (DMA). The blend's morphologies were investigated using scanning and transmission electron microscopies. Both DSC and DMA results suggested that PTT and PC were very limited, partially miscible pairs. The melting point, melt crystallization, and cold crystallization exotherms in the blends of PTT were depressed by the presence and amount of PC. When the PC content was <50 wt%, PC spherical particles were found to distribute evenly in the PTT matrix; at 50–60 wt%, the two‐phase structures were close to being bicontinuous. At higher PC content, PTT formed a string‐like texture in the PC matrix. The PTT spherulitic morphologies in PTT/PC blends were found to be very sensitive to PC and PC content. When the PC content was ≥60 wt%, the blends crystallized as an agglomeration of tiny PTT crystals.