Vibrational spectroscopy of ordered oxygen adiayers on Ni/Cu(001) and Co/Cu(001) thin film systems

We report surface vibrations in c(2 × 2) oxygen adlayers on Ni and Co thin films on a Cu(001) substrate measured at gG by high resolution EELS. For the Ni thin film surface, one phonon peak is measured for varying film thicknesses from 1.3 ML (monolayer) to 6 ML with a constant energy of 221 cm⁻¹. For the Co thin film surface, three loss peaks are found, whose relative intensities change as the film thicknesses are varied. One loss peak at ˜520 cm⁻¹ is tentatively assigned to the Fuchs-Kliewer mode of cobalt oxide (CoO). The other two peaks at 317 and 376 cm⁻¹ are likely related to different bonding sites. Surface phonons on the p(2 × 2) Co thin film (389 cm⁻¹) and a bulk resonance mode (115 cm⁻¹) are also reported.