Infrared modulated reflectance spectra of n and p type gallium antimonide and n type indium antimonide

We have observed the modulated reflectance spectra of n and p type GaSb at 300, 80, and 5 K from 0.56 to 2 eV. The modulated reflectance of intrinsic n type InSb was measured at 80 K from 0.2 to 2 eV. The “dry sandwich” vapor deposition technique was used to make the electroreflectance (ER) samples. The low-temperature spectrum of the undoped p type GaSb sample shows three peaks at the band edge that could be associated with transitions from the top of the valence band, the light (0.903 eV) and heavy (1.014eV) hole state Fermi levels to the conduction band. The energies of the observed peaks are in agreement with the Fermi level determination from Hall effect and Faraday rotation measurements. This modulation mechanism is based on band population effects. The ER signal of InSb under flatband condition at 80 K has five half oscillations at the direct band gap. The contribution of piezoelectric strain to ER is present since the dc bias required to achieve flatband condition is different at the band gap than at E₁. The ER signal corresponding to the direct gap energy E₀ and to the spin-orbit energy E₀ + Δ₀ was determined in the n and p type samples of GaSb at different temperatures. We have measured the intrinsic energy gap in GaSb at room temperature. E_g = 0.74 eV. The corresponding spin-orbit splitting was found to be Δ₀ = 0.733 ± 0.002 eV.