Synthesis of boron nitride coatings on quartz fibers: Thickness control and mechanism research |
| |
Authors: | Yu ZhengShubin Wang |
| |
Institution: | a School of Materials Science and Engineering, Beihang University, Beijing 100191, China b Key Laboratory of Aerospace Materials and Performance (Ministry of Education), School of Materials Science and Engineering, Beihang University, Beijing 100191, China |
| |
Abstract: | Boron nitride (BN) coatings were successfully synthesized on quartz fibers by dip-coating in boric acid and urea solutions at 700 °C. The SEM micrographs indicated that the quartz fibers were fully covered by coatings with smooth surface. The XRD, FT-IR, XPS spectra and HR-TEM results showed that the composition of the coatings which combined closely with the quartz fibers was polycrystalline h-BN. By changing the dip circles, the coating thickness was well controlled. The thicknesses of samples dipped less than six circles increased linearly with dipping-circles; and the increment of coating thickness would slow down when the fibers were dipped 10 circles. After being dipped for 10 circles, the thickness was about 300 nm. The coating thickness was also established by calculation and the calculated results were consistent with the results measured by micrograph. |
| |
Keywords: | Boron nitride Fiber coatings Dip-coating |
本文献已被 ScienceDirect 等数据库收录! |
|