A study of the effect of ZrO2 on the magnetic properties of FePt/ZrO2 multilayer

Fe_xPt_100−x(30 nm) and Fe_xPt_100−x(3 nm)/ZrO₂]₁₀ (x = 37, 48, 57, 63, 69) films with different ZrO₂ content were prepared by RF magnetron sputtering technique, then were annealed at 550 °C for 30 min. This work investigates the effect of ZrO₂ doping on the microstructural evolution, magnetic properties, grain size, as well as the ordering kinetics of FePt alloy films. The as-deposited films behaved a disordered state, and the ordered L1₀ structure was obtained by post-annealing. The magnetic properties of the films are changed from soft magnetism to hard magnetism after annealing. The variation of the largest coercivities of Fe_xPt_100−x/ZrO₂]₁₀ films with the Fe atomic percentage, x and differing amounts of ZrO₂ content reveals that as we increase the ZrO₂ content we must correspondingly increase the amount of Fe. This phenomenon suggests that the Zr or O atoms of ZrO₂ preferentially react with the Fe atoms of FePt alloy to form compounds. In addition, introducing the nonmagnetic ZrO₂ can reduce the intergrain exchange interactions of the FePt/ZrO₂ films, and the interactions are decreased as the ZrO₂ content increases, the dipole interactions are observed in FePt/ZrO₂ films as the ZrO₂ content is more than 15%.