The effect of chloride ions on the corroded surface layer of 00Cr22Ni5Mo3N duplex stainless steel under cavitation |
| |
Institution: | 1. School of Physics and Electronic Information/Information College, Huaibei Normal University, Huaibei, Anhui 235000, P R China;2. School of Life Science, Huaibei Normal University, Huaibei, Anhui 235000, P R China |
| |
Abstract: | The effects of Cl− on the corroded surface layer of 00Cr22Ni5Mo3N duplex stainless steel under cavitation in chloride solutions were investigated using nanoindentation in conjunction with XRD and XPS. The results demonstrate that Cl− had a strong effect on the nano-mechanical properties of the corroded surface layer under cavitation, and there was a threshold Cl− concentration. Furthermore, a close relationship between the nano-mechanical properties and the cavitation corrosion resistance of 00Cr22Ni5Mo3N duplex stainless steel was observed. The degradation of the nano-mechanical properties of the corroded surface layer was accelerated by the synergistic effect between cavitation erosion and corrosion. A key factor was the adsorption of Cl−, which caused a preferential dissolution of the ferrous oxides in the passive film layer on the corroded surface layer. Cavitation further promoted the preferential dissolution of the ferrous oxides in the passive film layer. Simultaneously, cavitation accelerated the erosion of the ferrite in the corroded surface layer, resulting in the degradation of the nano-mechanical properties of the corroded surface layer on 00Cr22Ni5Mo3N duplex stainless steel under cavitation. |
| |
Keywords: | Chloride ions Duplex stainless steel Nano-mechanical properties Corroded surface layer Cavitation corrosion Nanoindentation |
本文献已被 ScienceDirect 等数据库收录! |
|