Comparison of piezoelectricity in Ta and La substituted lead calcium titanate ceramics

This paper reports the experimental investigations on the effect of La³⁺ and Ta⁵⁺ substitution on the structural characteristics and dielectric and piezoelectric properties of lead calcium titanate (PCT) ceramic. The PCT samples with A-site and B-site substitution having the composition formula Pb_0.76−x/2La_xCa_0.24(Ti_0.98Mn_0.02)_1−x/2O₃ and Pb_0.76Ca_0.24Mn_0.02Ti _0.98−5x/4Ta_xO₃, x=0 and 0.02, respectively_, were prepared using conventional solid-state reaction method. Phase formation and structural analysis were studied using X-ray diffraction and scanning electron microscopy, respectively. Dielectric constant (ε′) and loss tangent (tan δ) as a function of frequency were measured at room temperature as well as elevated temperature. Both ε′ and tan δ decreased with increase in frequency at room temperature. Curie temperature decreased with La and Ta doping in PCT ceramics due to a decrease in the tetragonality of PCT ceramics. Piezoelectric charge coefficients (d₃₃, d₃₁) increased with La³⁺ substitution due to reorientation of the grains and decreased with Ta⁵⁺ substitution because of the increase in porosity. Figure of merit d_hg_h increased and decreased with La and Ta substitution, respectively. A good ferroelectric behaviour is obtained for La substitution, while no hysteresis is obtained for Ta substitution.