掺铥钨酸钡单晶生长和光谱研究

采用Czochralski 法生长出光学质量的BaWO₄:Tm³⁺单晶，利用X粉末衍射实验确定了不同掺杂浓度晶体的晶胞参数.测定了晶体的室温吸收光谱，应用Juud-Ofelt理论，拟合了光谱的3个强度参数，其值分别为Ω₂=404×10^-20cm²，Ω₄=0509×10^-20cm²，Ω关键词： 4：Tm³⁺单晶')" href="#">BaWO₄：Tm³⁺单晶 吸收谱 光谱参数 上转换发光

The growth and spectral characteristics of BaWO_4 :Tm~(3+) single crystal

The BaWO_4 : Tm~(3+) single crystals of optical quality have been grown by the Czochralski technique. The lattice parameters of crystals with different doping concentrations were determined by XRD. The absorption spectra were measured at room temperature. And the optical parameters, such as transition line intensity, oscillator strength and absorption section were calculated by using Juud-Ofelt theory. The three intensity parameters were fitted to be Ω_2 = 4.04 ×10~(-20) cm~2,Ω_4 = 0.509×10~(-20) cm~2, Ω_6 = 0.134 ×10~(-20) cm~2, respectively. The lifetime, branching ratio and integrated stimulated-emission cross section were obtained. Ultra-visible fluorescence was measured and analyzed. The red up-conversion luminescence with wavelengths 689 nm and 704 nm corresponding to the transition from ~3F_3 to ~3H_3 was observed under Ti-sapphire laser and LD laser, respectively.