| 喷墨打印和旋涂法制备有机电致发光显示器件中空穴注入及发光层的比较研究 |
| |
| 引用本文： | 陈文斌,郭文瑞,牟婉莹,杜真真,唐鹏宇,苏文明,张东煜.喷墨打印和旋涂法制备有机电致发光显示器件中空穴注入及发光层的比较研究[J].发光学报,2018,39(10):1451-1457. |
| |
| 作者姓名： | 陈文斌 郭文瑞 牟婉莹 杜真真 唐鹏宇 苏文明 张东煜 |
| |
| 作者单位： | 1. 中国科学院 苏州纳米技术与纳米仿生研究所, 江苏 苏州 215123;
2. 中国科学院大学, 北京 100049 |
| |
| 基金项目： | 国家重点研发计划（2017YFB0404403）资助项目 |
| |
| 摘 要： | 比较了喷墨印刷和旋涂PEDOT:PSS薄膜的表面性能，发现喷涂PEDOT:PSS薄膜上印有发射层油墨后，其表面性能有很大差异。在喷墨打印PEDOT:PSS膜的表面上只发现了大量的和类山状的聚合物颗粒。进一步的研究表明，形态的差异源于润湿性的不同。揭示了喷墨打印和旋涂对膜性能的不同影响，从而在喷墨打印PEDOT:PSS膜上构建了更精细的结构。
|
| 关 键 词： | 喷墨打印 有机发光二极管 多层印刷 表面形貌控制 |
| 收稿时间： | 2018-01-22 |
Comparing of Inkjet Printing Versus Spin Coating for Preparing Fine Structure Hole Transfer and Emitting Layers in OLED Display Construction |
| |
| CHEN Wen-bin,GUO Wen-rui,MOU Wan-ying,DU Zhen-zhen,TANG Peng-yu,SU Wen-ming,ZHANG Dong-yu.Comparing of Inkjet Printing Versus Spin Coating for Preparing Fine Structure Hole Transfer and Emitting Layers in OLED Display Construction[J].Chinese Journal of Luminescence,2018,39(10):1451-1457. |
| |
| Authors: | CHEN Wen-bin GUO Wen-rui MOU Wan-ying DU Zhen-zhen TANG Peng-yu SU Wen-ming ZHANG Dong-yu |
| |
| Institution: | 1. Printable Electronics Research Centre, Suzhou Institute of Nano-Tech and Nano-Bionics, Chinese Academy of Sciences, Suzhou 215123, China;
2. University of Chinese Academy of Sciences, Beijing 100049, China |
| |
| Abstract: | A comparison between the surface properties of inkjet printed and spin coated PEDOT:PSS films was made in consequence of the intriguing distinction after printing emitting layer inks on them. The sizable and hill-like polymer grains were only found on the surface of the inkjet printed PEDOT:PSS film. Further investigation demonstrated the difference in morphology stems from the diverse of wetting properties. The differing effects on film properties between inkjet printing and spin coating were revealed, according to which a finer structure was constructed on inkjet printed PEDOT:PSS film. |
| |
| Keywords: | inkjet printing organic light emitting diodes multilayer printing surface morphology control |
|