摘    要:实验采用碳酸锂、氧化钨、氧化铕制备了LiEuW2O8发光粉,通过扫描电镜和光谱仪分别研究了它的形貌与光谱特征。结果显示:LiEuW2O8发光粉的激发光谱较宽,非常适合于近紫外、蓝光及绿光芯片,发射光谱峰值位于615nm,色坐标为(x=0.666,y=0.331);球磨对它的形貌影响非常明显。为了比较硫化物发光粉和LiEuW2O8发光粉的性能,分别对他们进行了封装实验,结果显示:LiEuW2O8发光粉能够有效降低色温,更重要的是,它对光效影响较小,4000K时,光效可以保持在60lm/W以上。

关 键 词:LiEuW2O8  白光LED  封装  色温
收稿时间:2009-07-11

Preparation and Package Performances of Red Phosphor for LED
ZHANG Rui-xi,WANG Hai-bo,HUANG Ru-xi,XIE Ye,LIN Hai-feng.Preparation and Package Performances of Red Phosphor for LED[J].Chinese Journal of Luminescence,2010,31(3):305-310.
Authors:ZHANG Rui-xi  WANG Hai-bo  HUANG Ru-xi  XIE Ye  LIN Hai-feng
Institution:1. State Key Laboratory of Materials-Oriented Chemical Engineering, Nanjing University of Technology, Nanjing 210009, China;2. The Research Institute of Electric Light Source Materials of NJUT, Nanjing 210015, China
Abstract:LiEuW2O8 phosphor was prepared with lithium carbonate, europium oxide and tungsten oxide. The spectral properties and morphology were exhibited by fluorescence spectrometer and SEM, respectively. The result showed that there is a wide excitation spectrum of this phosphor being suitable for LED chips with near-ultraviolet ( NUV) , blue or green emission. Its emission peak locates at 613 nm, and the emission chromaticity coordinates are x =0.666 ,y = 0. 331;Milling obviously impacts on its morphology. Sulfide phosphor and LiEuW2O8 phosphor were encapsulated, respectively, to compare their properties, the result showed that the latter can also decrease color temperature, and more importantly,the luminous efficiency is less affected, it can keep 60 lm/W above when color temperature is 4 000 K.
Keywords:LiEuW2O8  LiEuW2O8  white LED  package  color temperature
本文献已被 CNKI 万方数据 等数据库收录!
点击此处可从《发光学报》浏览原始摘要信息
点击此处可从《发光学报》下载免费的PDF全文
设为首页 | 免责声明 | 关于勤云 | 加入收藏

Copyright©北京勤云科技发展有限公司  京ICP备09084417号