Intensive green emission of ZnAl2O4:Mn2+ under vacuum ultraviolet and low-voltage cathode ray excitation |
| |
| Authors: | Zhang Su Liang Hongbin Liu Yuewei Liu Yufeng Hou Dejian Zhang Guobin Shi Junyan |
| |
| Institution: | MOE Laboratory of Bioinorganic and Synthetic Chemistry, KLGHEI of Environment and Energy Chemistry, School of Chemistry and Chemical Engineering, Sun Yat-sen University, Guangzhou 510275, China. |
| |
| Abstract: | A series of Zn(1-x)Mn(x)Al(2)O(4) (x=0.001～0.08) phosphors were synthesized by a traditional solid-state reaction route. Their photoluminescence under vacuum ultraviolet (VUV, energy E>50000 cm(-1), wavelength λ<200 nm) and cathodoluminescence under low-voltage electron beam excitation were evaluated. The luminescence decays were also measured. The intense green emission was observed with a peak at about 510 nm upon 172/147 nm excitation. The luminescence of optimum phosphor Zn(0.99)Mn(0.01)Al(2)O(4) (ZAM) was compared with that of commercial green phosphor Zn(2)SiO(4):Mn(2+) (ZSM). The maximum emission intensity of ZAM is larger than that of ZSM under 172/147 nm and low-voltage electron beam excitation. The values of chromaticity coordinates reveal the phosphors can evidently enlarge the tricolor gamut. The results show that the ZnAl(2)O(4):Mn(2+) phosphors may be considered as candidates for Hg-free lamps, plasma flat backlights, and field emission backlights for liquid crystal displays. |
| |
| Keywords: | |
| 本文献已被 PubMed 等数据库收录！ |
|