Annealing effects on structure and laser-induced damage threshold of Ta2O5/SiO2 dielectric mirrors

The effects of annealing on structure and laser-induced damage threshold (LIDT) of Ta₂O₅/SiO₂ dielectric mirrors were investigated. Ta₂O₅/SiO₂ multilayer was prepared by ion beam sputtering (IBS), then annealed in air under the temperature from 100 to 400 °C. Microstructure of the samples was characterized by X-ray diffraction (XRD). Absorption of the multilayer was measured by surface thermal lensing (STL) technique. The laser-induced damage threshold was assessed using 1064 nm free pulsed laser at a pulse length of 220 μs.

It was found that the center wavelength shifted to long wavelength gradually as the annealing temperature increased, and kept its non-crystalline structure even after annealing. The absorbance of the reflectors decreased after annealing. A remarkable increase of the laser-induced damage threshold was found when the annealing temperature was above 250 °C.