Kalorimetrische messungen zur ermittlung der spezifischen grenzflächenenergie einer zweiphasigen Cu-7,5 At.-% In-legierung

With the help of a commercial heat-flux calorimeter the enthalpy change was measured as a function of the interlamellar spacing for lamellar precipitated Cu-In samples. This is related to the replacement of the two-phase structure (α + δ) by the homogeneous solid solution (α₀. From this, the specific interfacial enthalpy of the α-δ interface was determined to be ΔH^δ = 1100 ± 550 mJ m^?2. A value of ΔH^c = 1320 ± 60 J mol^?1 results for the chemical part of the total measured transformation enthalpy. A value of ΔS^δ = 0.66 mJ m^?2 K^?1 was estimated for the specific interfacial entropy and using the Gibbs-Helmholtz equation the specific interfacial free energy was calculated as ΔG^δ = 700 ± 400 mJ m^?2 at 600 K.