Relationship between electronic and crystal structure in Cu–Ni–Co–Mn–O spinels: Part A: Temperature-induced structural transformation

Local atomic and crystal structures around Cu and Mn atoms in Mn_1.68Cu_0.6Ni_0.48Co_0.24O₄ spinel samples fabricated by metal–organic decomposition synthesis at different annealing temperatures were investigated by X-ray absorption fine structure analysis. There are two distinct copper cations, Cu¹⁺ and Cu²⁺, both of which maintain tetrahedral coordination. The bond-length distances are Cu¹⁺–O = 2.00 Å and Cu²⁺–O = 1.80 Å. The manganese cations are for the most part octahedral. The spinels prepared at low temperature (600 °C) contain smaller (Mn⁴⁺–O = 1.88 Å) undistorted MnO₆ octahedrons corresponding to Mn⁴⁺ valence, whereas the manganese octahedrons in high-temperature materials (800 °C and higher) were larger and had a pronounced tetragonal distortion pertaining to Mn³⁺ oxidation state (Mn³⁺–O = 1.93 Å and 2.11 Å). By rising the fabrication temperatures, relative concentration of the species of Mn⁴⁺ and Mn³⁺ varies as a result of the reaction represented by Cu¹⁺ + Mn⁴⁺  Cu²⁺ + Mn³⁺, implying irreversible temperature-induced structural transformation. Atomic coordinates in the low-temperature phase are similar to those found in the ideal cubic spinel with oxygen parameter u = 0.27, whereas local environments of the Cu and Mn atom correspond to the tetragonal CuMn₂O₄ phase (space group I4₁/amd). Unlike in CuMn₂O₄, orientation of the lattice distortions is random, however, the long-range cubic spinel structure is retained at all time.