| 光致变色含氟丙烯酸酯涂层的制备及性能 |
| |
| 引用本文： | 符柳娃,苏嘉辉,严佳进,张婷,杨妍,刘晓暄. 光致变色含氟丙烯酸酯涂层的制备及性能[J]. 应用化学, 2018, 35(12): 1434-1441. DOI: 10.11944/j.issn.1000-0518.2018.12.180014 |
| |
| 作者姓名： | 符柳娃 苏嘉辉 严佳进 张婷 杨妍 刘晓暄 |
| |
| 作者单位： | 广东工业大学材料与能源学院,高分子化学与物理系 广州 510006;闽南师范大学化学与环境学院 福建 漳州 363000 |
| |
| 基金项目： | 广东省(广州市)科技厅(局)科学计划重大(重点)项目(2005B010122005,2015B090925008,20150122)资助 |
| |
| 摘 要： | 选取十二烷基硫酸钠(SDS),辛基苯基聚氧乙烯醚(OP-10)为复合乳化剂,过硫酸钾(KPS)为引发剂,将2-(全氟己基)乙基甲基丙烯酸酯(PFM)与丙烯酸酯类单体采用预乳化-半连续种子乳液聚合法进行乳液共聚,再将羟基螺吡喃(SPOH)与乳液进行物理共混,制得光致变色含氟丙烯酸酯乳液。 通过多种表征手段研究丙烯酸正丁酯(n-BA)和甲基丙烯酸甲酯(MMA)软硬单体的质量比,SPOH的用量对聚合反应和乳胶膜性能的影响。 结果表明,加入含氟单体后乳胶膜与水、油的接触角提高,热稳定性提高;加入SPOH的质量分数为1.25%时,乳胶膜具有较好的光致变色性能。
|
| 关 键 词： | 乳液聚合 光致变色 含氟丙烯酸酯 螺吡喃 |
| 收稿时间： | 2018-01-17 |
Preparation and Properties of Photochromic Fluoroacrylate Coating |
| |
| FU Liuwa,SU Jiahui,YAN Jiajin,ZHANG Ting,YANG Yan,LIU Xiaoxuan. Preparation and Properties of Photochromic Fluoroacrylate Coating[J]. Chinese Journal of Applied Chemistry, 2018, 35(12): 1434-1441. DOI: 10.11944/j.issn.1000-0518.2018.12.180014 |
| |
| Authors: | FU Liuwa SU Jiahui YAN Jiajin ZHANG Ting YANG Yan LIU Xiaoxuan |
| |
| Affiliation: | Department of Polymeric Materials and Engineering,School of Materials and Energy,Guangdong University of Technology,Guangzhou 510006,China;College of Chemistry and Environment,Minnan Normal University,Zhangzhou,Fujian 363000,China |
| |
| Abstract: | The fluorine modified acrylate emulsion polymerization was performed using sodium dodecyl sulfate(SDS) and octylphenyl polyoxyethylene ether(OP-10) as complex emulsifiers, 2-(perfluorohexyl) ethylmethacrylate(PFM) as the fluorinated acrylate monomer, and potassium persulfate(KPS) as the initiator. Spiropyran was physically blended with the emulsion to obtain a photochromic fluorinated acrylate emulsion. The effects of the mass ratio of methyl methacrylate(MMA) to butyl acrylate(BA) monomers, and the amount of hydroxyspiropyran(SPOH) on the polymerization and the properties of the latex films were studied by means of various spectroscopic methods. The results show that the contact angle and thermal stability of the fluorinated polyacrylate are improved. The film presents good photochromic properties with addition of 1.25%(mass fraction) spiropyran. |
| |
| Keywords: | emulsion polymerization photochromic fluorinated acrylate spiropyran |