Photodegradation of polyethylene in the presence of ferric chloride

Effects of ferric chloride (FeCl₃) on photodegradation of high-density polyethylene (PE) were investigated by using ESR and infrared spectrometry. In the system with irradiation at light of λ > 220 nm, PE irradiated at 77°K yielded an 8-line spectrum, the intensity of which was markedly weakened by using FeCl₃ with the sample, indicating a distinct depression of radical formation. On the other hand, PE with the use of FeCl₃ yielded radicals under irradiation only with light of λ > 300 nm, showing a singlet spectrum with a line width of 15 gauss. For photooxidized PE, almost the same effect of FeCl₃ was observed. On irradiation at room temperature, PE samples with and without FeCl₃ showed a singlet spectrum with line widths of 15 and 25 gauss, respectively. On the other hand, the unsaturated double bond contained in a small amount in PE sample was observed by infrared study to be decreased with photoirradiation; however, the decrease was sharply depressed with the addition of FeCl₃ to the sample. The degradation of carbonyl group in a photooxidized sample was markedly affected by photoirradiation, and the decay was obviously reduced for the sample on addition of FeCl₃. It is concluded that FeCl₃ works upon photodegradation of PE to enhance the Norrish type II reaction and to accelerate the formation of unsaturated double bond in the chain.