Improvement of electrochemical performance for Li-rich spherical Li1.3[Ni0.35Mn0.65]O2+x modified by Al2O3

The Li-rich Li_1.3Ni_0.35Mn_0.65]O_2+x microspheres are firstly prepared and subsequently transferred into the Al₂O₃-coated Li-rich Li_1.3Ni_0.35Mn_0.65]O_2+x microspheres by a simple deposition method. The as-prepared samples are characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), cyclic voltammetry (CV), electrochemical impedance spectroscopy (EIS), and charge/discharge tests. The results reveal that the Al₂O₃-coated Li-rich Li_1.3Ni_0.35Mn_0.65]O_2+x sample has a typical α-NaFeO₂ layered structure with the existence of Li₂MnO₃-type integrated component, and the Al₂O₃ layer is uniformly coated on the surface of the spherical Li-rich Li_1.3Ni_0.35Mn_0.65]O_2+x particles with a thickness of about 4 nm. Importantly, the Al₂O₃-coated Li-rich sample exhibits obviously improved electrochemical performance compared with the pristine one, especially the 2 wt.% Al₂O₃-coated sample shows the best electrochemical properties, which delivers an initial discharge capacity of 228 mAh g^?1 at a rate of 0.1 C in the voltage of 2.0–4.6 V, and the first coulombic efficiency is up to 90 %. Furthermore, the 2 wt.% Al₂O₃-coated sample represents excellent cycling stability with capacity retention of 90.9 % at 0.33 C after 100 cycles, much higher than that of the pristine one (62.2 %). Particularly, herein, the typical inferior rate capability of Li-rich layered cathode is apparently improved, and the 2 wt.% Al₂O₃-coated sample also shows a high rate capability, which can deliver a capacity of 101 mAh g^?1 even at 10 C. Besides, the thin Al₂O₃ layer can reduce the charge transfer resistance and stabilize the surface structure of active material during cycling, which is responsible for the improvement of electrochemical performance of the Li-rich Li_1.3Ni_0.35Mn_0.65]O_2+x .