Synthesis of high surface area nanometer magnesia by solid-state chemical reaction

Nanometer MgO samples with high surface area, small crystal size and mesoporous texture were synthesized by thermal decomposition of MgC₂O₄ · 2H₂O prepared from solid-state chemical reaction between H₂C₂O₄ · 2H₂O and Mg (CH₃COO)₂ · 4H₂O. Steam produced during the decomposition process accelerated the sintering of MgO, and MgO with surface area as high as 412 m² · g⁻¹ was obtained through calcining its precursor in flowing dry nitrogen at 520°C for 4 h. The samples were characterized by X-ray diffraction, N₂ adsorption, transmission electron microscopy, thermogravimetry, and differential thermal analysis. The as-prepared MgO was composed of nanocrystals with a size of about 4–5 nm and formed a wormhole-like porous structure. The MgO also had good thermal stability, and its surface areas remained at 357 and 153 m²·g⁻¹ after calcination at 600 and 800°C for 2 h, respectively. Compared with the MgO sample prepared by the precipitation method, MgO prepared by solid-state chemical reaction has uniform pore size distribution, surface area, and crystal size. The solid-state chemical method has the advantages of low cost, low pollution, and high yield, therefore it appears to be a promising method in the industrial manufacture of nanometer MgO. Translated from Chinese Journal of Catalysis, 2006, 27(9): 793–798 (in Chinese)