Cathodic and anodic pre-treated boron doped diamond with different sp content: Morphological,structural, and impedance spectroscopy characterizations

In this work, the influence of cathodic (Red) and anodic (Ox) pre-treatment on boron doped diamond (BDD) films grown with different sp²/sp³ ratios was systematically studied. The sp²/sp³ ratios were controlled by the addition of CH₄ of 1,3,5 and 7 sccm in the gas inlet during the growth process. The electrodes were treated in 0.5 mol L⁻¹ H₂SO₄ at −3 and 3 V vs Ag/AgCl, respectively, for 30 min. The electrochemical response of BDD films was investigated using electrochemical impedance spectroscopy (EIS) and Mott–Schottky Plot (MSP) measurements. Four film sample sets were produced in a hot filament chemical vapor deposition reactor. During the growth process, an additional H₂ line passing through a bubbler containing the B₂O₃ dissolved in methanol was used to carry the boron. The scanning electron microscopy morphology showed well faced films with a small decrease in their grain size as the CH₄ concentration increased. The Raman spectra depicted a pronounced sp² band, mainly for films with 5 and 7 sccm of CH₄. MSP showed a decrease in the acceptor concentration as the CH₄ increased indicating the CH₄ influence on the doping process for Red–BDD and Ox–BDD samples. Nonetheless, an apparent increase in the acceptor concentrations for both Ox–BDD samples was observed compared to that for Red–BDD samples, mainly attributed to the surface conductive layer (SCL) formation after this strong oxidation process. The EIS Nyquist plots for Red–BDD showed a capacitance increase for the films with higher sp² content (5 and 7 sccm). On the other hand, the Nyquist plots for Ox–BDD can be described as semicircles near the origin, at high frequencies, where their charge transfer resistance strongly varied with the sp² increase in such films.