Preparation, crystal structure, and photoluminescence of Ca2SnO4:Eu, Y

Eu³⁺-doped Ca₂SnO₄ (solid solutions of Ca_2−xEu_2xSn_1−xO₄, 0?x?0.3) and Eu³⁺ and Y³⁺-codoped Ca₂SnO₄ (Ca_1.8Y_0.2Eu_0.2Sn_0.8O₄) were prepared by solid-state reaction at 1400 °C in air. Rietveld analysis of the X-ray powder diffraction patterns revealed that Eu³⁺ replaced Ca²⁺ and Sn⁴⁺ in Eu³⁺-doped Ca₂SnO₄, and that Eu³⁺ replaced Ca²⁺ and Y³⁺ replaced Sn⁴⁺ in Ca_1.8Y_0.2Eu_0.2Sn_0.8O₄. Red luminescence at 616 nm due to the electric dipole transition ⁵D_o→⁷F₂ was observed in the photoluminescence (PL) spectra of Ca_2−xEu_2xSn_1−xO₄ and Ca_1.8Y_0.2Eu_0.2Sn_0.8O₄ at room temperature. The maximum PL intensity in the solid solutions of Ca_2−xEu_2xSn_1−xO₄ was obtained for x=0.1. The PL intensity of Ca_1.8Y_0.2Eu_0.2Sn_0.8O₄ was 1.26 times greater than that of Ca_2−xEu_2xSn_1−xO₄ with x=0.1.