Thermodynamic properties of lithium mica: Lepidolite

Calorimetric measurements were made on natural sample of lepidolite having the composition (K_0.80Na_0.05Ca_0.07Rb_0.16Cs_0.03)(Li_1.34Al_1.40Fe³⁺_0.01)[Si_3.25Al_0.75O₁₀]F_1.80(OH)_0.20 from Na-Li-type rare-element-rich pegmatites of East Sayany, Russia. High-temperature enthalpy increments were measured with a Tian-Calvet calorimeter at 444-972 K using the drop method. The resultant (T) equation in the interval T = 298.15-972 K was calculated:  = 316.10 + 228.12 × 10⁻³ T − 50.10 × 10⁵ T⁻² (J K⁻¹ mol⁻¹) [± 0.4%] and the value of (298.15 K) = 327.8 J K⁻¹ mol⁻¹ was obtained. The standard molar enthalpy of formation from the elements was determined by high-temperature drop solution calorimetry in molten lead borate at T = 973 K. The value of Δ_f(298.15 K) for lepidolite was found to be −6201 ± 18 kJ mol⁻¹. The thermodynamic properties of lepidolite of idealized composition KLi_1.5Al_1.5[Si₃AlO₁₀]F₂ were estimated based on the experimental data obtained.