Thermal conductivity of La0.67(CaxSr1−x)0.33MnO3 (x=0, 0.5, 1) and La0.6Y0.07Ca0.33MnO3 pellets between 10 and 300 K

Thermal conductivity (λ) of nanocrystalline La_0.67(Ca_xSr_1−x)_0.33MnO₃ (x=0, 0.5, 1) and La_0.6Y_0.07Ca_0.33MnO₃ pellets prepared by a novel ‘pyrophoric’ method have been studied between the temperature range 10 and 300 K. Our data show that the magnitude of thermal conductivity is strongly influenced by the ion substitutions at La-site. The analysis of the thermal conductivity data indicates that the thermal transport is governed largely by phonons scattering in these systems and the electronic contribution is as small as 0.2-1% of total thermal conductivity (λ_total). At low temperatures (<90 K) 2D like lattice defects contribute to the phonon scattering dominantly and its strength increases with increasing Sr content and also with partial substitution of La by Y. Depending upon the composition of the samples, the magnon thermal conductivity contributes 2-15% of λ_total close to T_C. In the paramagnetic regime the unusual increase in λ_total keeps signature of large dynamic lattice distortion.