A Bridge-Linked Phosphorus-Containing Flame Retardant for Endowing Vinyl Ester Resin with Low Fire Hazard
Authors:Zihui Xu  Jing Zhan  Zhirong Xu  Liangchen Mao  Xiaowei Mu  Ran Tao
Affiliation:1.School of Civil Engineering, Anhui Jianzhu University, Hefei 230601, China;2.State Key Laboratory of Fire Science, University of Science and Technology of China, Hefei 230026, China;3.Anhui Province Key Laboratory of Human Safety, Hefei 230601, China
Abstract:
The high flammability of vinyl ester resin (VE) significantly limits its widespread application in the fields of electronics and aerospace. A new phosphorus-based flame retardant 6,6’-(1-phenylethane-1,2 diyl) bis (dibenzo[c,e][1,2]oxaphosphinine 6-oxide) (PBDOO), was synthesized using 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO) and acetophenone. The synthesized PBDOO was further incorporated with VE to form the VE/PBDOO composites, which displayed an improved flame retardancy with higher thermal stability. The structure of PBDOO was investigated using Fourier transformed infrared spectrometry (FTIR) and nuclear magnetic resonances (NMR). The thermal stability and flame retardancy of VE/PBDOO composites were investigated by thermogravimetric analysis (TGA), vertical burn test (UL-94), limiting oxygen index (LOI), and cone calorimetry. The impacts of PBDOO weight percentage (wt%) on the flame-retardant properties of the formed VE/PBDOO composites were also examined. When applying 15 wt% PBDOO, the formed VE composites can meet the UL-94 V-0 rating with a high LOI value of 31.5%. The peak heat release rate (PHRR) and the total heat release (THR) of VE loaded 15 wt% of PBDOO decreased by 76.71% and 40.63%, respectively, compared with that of untreated VE. In addition, the flame-retardant mechanism of PBDOO was proposed by analyzing pyrolysis behavior and residual carbon of VE/PBDOO composites. This work is expected to provide an efficient method to enhance the fire safety of VE.
Keywords:vinyl ester resin   flame retardant   thermal stability   mechanism analysis
设为首页 | 免责声明 | 关于勤云 | 加入收藏

Copyright©北京勤云科技发展有限公司  京ICP备09084417号