Synthesis of bimodal porous structured TiO2 microsphere with high photocatalytic activity for water treatment |
| |
| Authors: | Pei Fung Lee Xiwang Zhang Darren D Sun Jianhong Du James O Leckie |
| |
| Institution: | aSchool of Civil and Environmental Engineering, Nanyang Technological University, Singapore 639798, Singapore;bDepartment of Civil and Environmental Engineering, School of Engineering, Stanford University, Stanford, CA 94305-4020, USA |
| |
| Abstract: | In this work bimodal structured titanium dioxide (TiO2) microsphere has been prepared from commercial TiO2 powder and nano-sized titania gel via sol–gel spray-coating technique. Crystallization and transformation behavior of titania gel were investigated. The results revealed that the crystallization and transformation of anatase particles were substantially affected by the concentration of solvent and calcination temperature. Anatase crystallite size of 10 nm was obtained at mole ratio of solvent/precursor 50/1 and calcination temperature of 450 °C. The prepared nano-sized titania gel was embedded within the core (commercial TiO2, P25) during the spraying process. The prepared TiO2 microsphere was characterized using X-ray diffractometer (XRD), scanning electron microscope (SEM), field emission electron microscope (FESEM) and micropore analysis. The photocatalytic activity was monitored by following the degradation of phenol with activity benchmarked against commercial P25 (Degussa). The increase of photocatalytic activity of TiO2 microsphere was attributed to the nano-sized anatase crystallite which has been incorporated into the TiO2 microsphere. |
| |
| Keywords: | TiO2 microsphere Spray-coating |
| 本文献已被 ScienceDirect 等数据库收录！ |
|