Structural and compositional changes in ion-bombarded Ta2O5

A detailed study of the effect of heavy-ion bombardment on Ta₂O₅ has been undertaken using a combination of radioactive tracer techniques, electron microscopy, and Rutherford backscattering. Crystalline Ta₂O₅ is amorphized at ~6 × 10¹³ ions cm^?2, while at a dose of ~5 × 10¹⁶ ions cm^?2 the electron microscopy reveals the development of random grains of a new crystalline phase. By ~1 × 10¹⁷ ions cm^?2 the grains are not yet overlapping but still yield a diffraction pattern consistent with either δ-Ta-O (not to be confused with TaO) or Ta_1?xO₂, thus indicating that Ta₂O₅, like most other transition-metal oxides, is subject to preferential sputtering. Preferential sputtering was confirmed by backscattering analysis of specimens bombarded to high doses, where the average surface composition was found to be Ta_1.8±0.2O₂ or, equivalently, Ta₂O_2.2±0.2. The surface alteration had an average composition independent of the mass and energy of the incident ions.