负载型La0.8Sr0.2MnO3燃烧催化剂的载体效应

The Effects of Support on Loaded Combustion Catalyst of La0.8Sr0.2MnO3

Combustion catalysts La0.8Sr0.2MnO3 supported on γ-Al2O3, α-Al2O3, cordierite (2MgO?2Al2O3?5SiO2) and ZrO2 were compared. Further investigation was focused on LSM/ γ-Al2O3 catalyst. It was observed that LSM/γ－Al2O3 catalyst loaded with 20% (mass fraction) LSM (La0.8Sr0.2MnO3 or corresponding oxides), heated at 750℃ or above, perovskite-type oxides were found by XRD examination, whereas, the same catalyst loaded with 10% or less LSM, perovskite oxides were absent, calcination temperature about 750℃ is necessary for the formation of perovskite structure in LSM/γ-Al2O3 catalysts. High activity of complete oxidation of xylen will be obtained when perovskite-type oxides.
Investigation of TPR showed that neat LSM or LSM/γ-Al2O3(20%) was reduced by H2-N2 mixed gas. Two degradation processes took place. In the first, reduced temperature peak was about 350 - 450℃. If reduction ended at 400℃, perovskite structure was retained, which may be due to the reduction of Mn3+to Mn2+ on the surface of LSM only. In the second process, perovskite structure was destroied, and La2O3, Mn2O3, Mn - Sr - O oxides could be obtained, which took place in the temperature range 685 - 750℃ and ended at 800℃. This was proved by TPR experiments (Fig. 3, 5) and XRD patterns (Fig. 4)
Catalysts LSM/γ-Al2O3(10% or 20%) heated at 500℃ have only one TPR peak, i. e. lower temperature peak. This is due to the absence of perovskite-type oxides in the catalysts. However, neat LSM or LSM/γ-Al2O3(20%) heated 750℃ or above, not only the first low temperature TPR peak but also the second peak, which is contributed by the perovskite-type oxides in these catalysts appeared. Therefore, the second TPR peak, i. e. the higher temperatue peak is a characteristic peak for perovskite-type oxides in the reduced process. When LSM/ γ-Al2O3 (10%) catalys is heated at 750℃, no perovskite-type oxides were detected by XRD, and the second reduction peak was absent also in TPR process. \
The order of the second reduction peak temperature(characteristic peak of perovskite - type ox- ides) is: neat LSM(750℃）> LSM/γ-Al2O3 20% (685-698℃) -deposited LSM/γ-Al2O3 (698℃) > LSM/γ-Al2O3 15% (677 - 680℃) >(LSM/γ-AL2O3 10% 620 - 630℃, for Mn - Al - O medium oxides on surface). It is correleted with the increasing of the effect of support sequentially.
When LSM/γ-Al2O3 catalysts were heated at 900℃, more stable phase, spinel MnAl2O4 appeared, which could be proved by TPR of model catalyst MnAl2O4/γ-Al2O3.