| Abstract: | Calcium phosphate based bioceramics, mainly in the form of hydroxyapatite (HA), have been in use in medicine and dentistry for the last 20 years. Applications include coatings of orthopaedic and dental implants, alveolar ridge augmentation, maxillofacial surgery, otolaryngology, and scaffolds for bone growth and as powders in total hip and knee surgery. These materials exhibit several problems of handling and fabrication, which can be overcome by mixing with a suitable binder. In this paper, mechanical alloying has been used successfully to produce nanocrystalline powders of HA using five different experimental procedures. The milled HA were studied by X-ray powder diffraction, infrared and Raman scattering spectroscopy. For four different procedures, HA was obtained after a couple of hours of milling (on an average, 20 h of milling depending on the reaction procedure). The XRD patterns indicate that the grain size is within the range of 29-103 nm. This milling process, used to produce HA, presents the advantage that melting is not necessary and the powder obtained is nanocrystalline with extraordinary mechanical properties. The material can be compacted and transformed in solid ceramic samples. The high efficiency of the process opens a way to produce commercial amount of nanocrystalline HA. Due to the nanocrystalline character of this powder, their mechanical properties have changed and for this reason a pressure of 1 GPa is enough to shape the sample into any geometry. |