Synthesis of the Dy: SrMoO4 with High Photocatalytic Activity under Visible Light Irradiation

Dysprosium (Dy)‐doping SrMoO₄ (with different molar ratio of Dy/Sr = 0/100, 10/100, 15/100 and 20/100) have been synthesized by high temperature thermal decomposition of metal–organic salt in organic solvent with a high boiling point. Their structures, morphology, and optical properties were characterized by X‐ray diffraction (XRD), high‐resolution tuning electron microscopy ((HR)TEM), X‐ray photo‐electron spectroscopy (XPS), and UV–vis diffuse reflectance spectroscopy (UV–vis DRS). Using this method, the pure phase, nano‐size, and low band gap of SrMoO₄ sample are obtained. The results shows that the size of as‐synthesized SrMoO₄ nanoparticles was about 200 nm. The band gap of Dy‐doped SrMoO₄ ranges from 3.76–3.90 eV, and decreases with increasing Dy concentration. The photocatalytic performance of as‐syntheszied products were determined from the degradation of methylene blue (MB) by UV–vis light irradiation. The 15 mol%Dy‐doped SrMoO₄ sample shows the best performance for photocatalytic degradation of methyl blue of nearly 100% in 120 min under visible irradiation, which is higher than most of those reported before. The present work is meaningful for revealing the underlying mechanism in photocatalyst and improving the photocatalytic performance.