The effect of different temperature annealing on phase relation of LaFe11.5Si1.5 and the magnetocaloric effects of La0.8Ce0.2Fe11.5−xCoxSi1.5 alloys

The phase relation of LaFe_11.5Si_1.5 alloys annealed at different high-temperature from 1223 K (5 h) to 1673 K (0.5 h) has been studied. The powder X-ray diffraction (XRD) patterns show that large amount of 1:13 phase begins to form in the matrix alloy consisting of α-Fe and LaFeSi phases when the annealing temperature is 1423 K. In the temperature range from 1423  to 1523 K, α-Fe and LaFeSi phases rapidly decrease to form 1:13 phase, and LaFeSi phase is rarely observed in the XRD pattern of LaFe_11.5Si_1.5 alloy annealed at 1523 K. With annealing temperature increasing from 1573  to 1673 K, the LaFeSi phase is detected again in the LaFe_11.5Si_1.5 alloy, and there is La₅Si₃ phase when the annealing temperature reaches 1673 K. There almost is no change in the XRD patterns of LaFe_11.5Si_1.5 alloys annealed at 1523 K for 3-5 h. According to this result, the La_0.8Ce_0.2Fe_11.5−xCo_xSi_1.5 (0≤×≤0.7) alloys are annealed at 1523 K (3 h). The analysis of XRD patterns shows that La_0.8Ce_0.2Fe_11.5xCo_xSi_1.5 alloys consist of the NaZn₁₃-type main phase and α-Fe impurity phase. With the increase of Co content from x=0 to 0.7, the Curie temperature T_C increases from 180 to 266 K. Because the increase of Co content can weaken the itinerant electron metamagnetic transition, the order of the magnetic transition at T_C changes from first to second-order between x=0.3 and 0.5. Although the magnetic entropy change decreases from 34.9 to 6.8 J/kg K with increasing Co concentration at a low magnetic field of 0-2 T, the thermal and magnetic hysteresis loss reduces remarkably, which is very important for the magnetic refrigerant near room temperature.