Effect of pH value on the structural and magnetic properties of nanocrystalline strontium hexaferrite thin films

Strontium hexaferrite SrFe₁₂O₁₉ thin films have been synthesized at different pH, adjusted by NH₄OH, on the Si (1 0 0) substrate using a spin coating sol-gel process. Fourier transform infrared spectroscopy analysis and theoretical calculations were conducted for determination and controlling metal citrates in solution precursors. X-ray diffraction, scanning electron microscopy and vibrating sample magnetometer were applied to evaluate the composition, microstructure, crystallite size and magnetic properties of the SrFe₁₂O₁₉ thin films. Using the solution with pH 7, the approximately single phase strontium hexaferrite thin films with optimum physical properties can be obtained at calcination temperature of 800 °C. The SrFe₁₂O₁₉ thin films derived from the solution with pH 7 after calcination at 800 °C exhibited crystallite size of 42 nm and magnetic properties of M_s=267 emu/cm³ (at 10 kOe), M_r=134 emu/cm³ and H_c=4290 Oe.